WITH GOOD THERMOSTABILITY, CORROSION RESISTENCE, THERMAL SHOCK RESISTANCE, HIGH MECHANICAL STRENGTH, EXCELLENT ELECTRICAL PROPERTY, CERAMIC PARTS ARE WIDELY USED IN INDUSTRIAL EQUIPMENT MANUFACTURING INDUSTRIES.
ALL PRODUCTS CAN PASS THE GERMAN STANDARD: DIN43724/DIN43725/DIN40680
NO. | Property | Unit | Alumina |
1 | Al2O3 | % | >99.3 |
2 | SiO2 | % | - |
3 | Density | g/cm3 | 3.88 |
4 | Water absorption | % | 0.01 |
5 | Cold compressive strength | MPa | 350 |
6 | 20ºC leakage rates | Torr/L.sec | <10-11 |
7 | Twisting in high temperature | mm | 0.2 allowed in 1600ºC |
8 | Bonding in high temperature |
| not bonded in 1600ºC |
9 | 20-1000ºC coefficient ofthermalexpansion | mm.10-6/ºC.m | 8.2 |
10 | Thermal conductivity | W/m.k | 25 |
11 | Electric insulation strength | KV/mm | 20 |
12 | 20ºCdirect current insulation resistance | Ohm/cm | 1014 |
13 | High-temperature insulation resistance | 1000ºC MΩ | ≥0.08 |
1300ºC MΩ | ≥0.02 | ||
14 | Thermal shock resistance |
| 4 times not cracked in 1550ºC |
15 | Maximum working temperature | ºC | 1800 |