High alumina ceramic honeycomb ceramic heater ceramic integral heater

Ceramic Honeycomb Heater Description:Honeycomb ceramic is composed of countless equal holes. The structure of it is like honeycomb shape and it is a kind of new ceramic products. The biggest hole number of it has reached 20~40 per square centimeter, the density is 4~6 grams per cubic centimeter and the water absorption rate is a

Featured Products

Ceramic Honeycomb Heater Description:
Honeycomb ceramic is composed of countless equal holes. The structure of it is like honeycomb shape and it is a kind of new ceramic products. The biggest hole number of it has reached 20~40 per square centimeter, the density is 4~6 grams per cubic centimeter and the water absorption rate is above 20%.
 
Porous Cordierite Honeycomb Monolith
Ceramic honeycomb used for RTO application
Cordierite is a magnesium alumina silicate material, which has very low linear expansion, low coefficient of thermal expansion and excellent resistance to thermal shock. Cordierite also offers an excellent range of mechanical strength, porosity criteria, and excels in cost-effective extruded and dry-pressed forms.
Cordierite Honeycomb Monoliths are divided into two types: porous type and compact type.

Application:
Widely used in chemical industry, electric power industry, metallurgy industry, petroleum industry,electronics industry,machinery industry,etc. The development prospect is considerable.

Features:
1.High strength.
2.High temperature resistance.
3.Corrosion resistance.
4.Wear resistance.
5.Good thermal conductivity.             
6.Environmentally friendly.

High Alumina porcelain Honeycomb Ceramic Heater Ceramic Monolith Heater
High Alumina porcelain Honeycomb Ceramic Heater Ceramic Monolith Heater
High Alumina porcelain Honeycomb Ceramic Heater Ceramic Monolith Heater

Spec.Quantity of channelsWall thickness (mm)Surface area (m2/m3)Free volume (%)Average weight (min.) (kg/m3)
150*150*30060*600.5131570680
150*150*30050*500.7105058680
150*150*30040*400.788365518
150*150*30025*251.057367502
 
Data&ItemHight Frequency Ceramic75% Ceramic95%  Ceramic99% CeramicTitanium OxideZirconiaMulliteComment
ContentTalc 85%alumina≥75%alumina≥95%alumina≥99%Titanium Oxide≥90%Zirconia≥90%3ALz032si02 
Fring temperature(Degree C)1350±201400-14501650-16801780-18001450±201550-16001260-1540 
Proportion(g/cm)2.83.2≥3.6≥3.8≥3.7>63.25 
Dielectric Strength(kv/mm)15131515 15 Volume density
Water absorption(%)<0.02<0.015<0.01<0.01<0.01<0.01<0.01 
Compressive Strength56022002400370072005000  
Hardness(HRA)≥75≥75≥82≥88≥80≥8565-70 
Volume Resistance(cm)≥1012>1012>1012>1012<1012>1012≥101225Degree C
Bending Strength(MPA)126280320400150700180 
Thermal Expansion(*10)6-7.566.2-8.56.8-8 9-104-4.425Degree C-700Degree C
Permittivity(MHZ)65.58.59.5  7 
Roughness(Ra)  ≤0.8≤0.8<0.1   
Mirror Polish  <0.3≤0.1≤0.05≤0.03  